PREPARATION
Fully assembled container shall be automatically abrasive blasted to SA 2 ½ according to Swedish standard SIS 05 05900. The blast profile to be in accordance with Bn9a shall be apprx. 50 microns. Particular attention shall be paied to the under frame in the shot blasting booth. The container shall be lifted to enable access to the under frame. All metal preparation shall be carried out just prior to assembly. Dry film thickness shall be established on accordance with with ISO 2808, DS/R 454, SSPC-PA 2 and DIN 55928 Teil 2.

PAINT-SYSTEM
Hempel A/S, 2800 Lyngby, Denmark

Primer:
HEMPADUR PRIMER 1536 two component epoxy zinc rich primer.
dry film thickness 40 microns

Topcoat
HEMPATEX 4641 - RAL Code to be advised
dry film thickness 80 microns
total minimum dry film thickness 120 microns

Primer
HEMPADUR PRIMER 1536 two component epoxy zinc rich primer.
dry film thickness 30 microns

Topcoat
HEMPADUR HB 4522 two component, high build epoxy paint - RAL code to be advised
dry film thickness 50 microns
total minimum dry film thickness 80 microns

 

Primer
HEMPADUR PRIMER 15300-19830 two component polyamide cured zinc phosphate solvent primer.
dry film thickness 40 microns

Finish coat
HEMPINOL 10220-19990
dry film thickness 175 microns
total minimum dry film thickness 215 microns
The dry film thickness specified is minimum.